7001 aluminum bar rod introduction
7001 aluminum bar rods are generally added with a small amount of copper, chromium and other alloys. They are known as the best products in aluminum alloys. They have high strength and are far better than mild steel. This alloy also has good mechanical properties and anode reaction. The addition of magnesium to the 7001 aluminum bar rod alloy containing 3%-7.5% zinc can form MgZn2 with ficant strengthening effect, which makes the heat treatment effect of this alloy far better than aluminum-zinc binary alloy.
Related parameters of 7001 aluminum bar rod
| chemical composition | Cu | Mn | Mg | Zn | Cr | Ti | Si | Fe | Al |
| 0.15～0.4 | 0.15 | 0.8～1.2 | 0.25 | 0.04～0.35 | 0.15 | 0.4～0.8 | 0.7 |
| Mechanical properties |
tensile strength &;b (MPa) |
Yield Strength &;0.2 (MPa) |
Elongation δ5 (％) |
Sample size | Coefficient of elasticity | Ultimate bending strength | Bearing yield strength | Poisson's ratio | Fatigue strength |
| ≥180 | ≥110 | ≥14 | diameter≤150 | 68.9 GPa | 228 MPa | 103 MPa | 0.330 | 62.1 MPa | |
The product specifications are complete, the price is favorable, the packaging is intact, the copper is pure, the straightness is good, and the inventory is large. Material certification and SGS report can be provided.
Features of 7001 aluminum alloy bar rod
The addition of magnesium to the 7001 aluminum alloy rods containing 3%-7.5% zinc alloy can form MgZn2 with ficant strengthening effect, making the alloy's heat treatment effect far better than aluminum-zinc binary alloys. 7001 aluminum bar rods are generally added with a small amount of copper, chromium and other alloys. They are known as the best products in aluminum alloys. They have high strength and are far better than mild steel. This alloy also has good mechanical properties and anode reaction.