6082 T6 cold drawn extruded aluminum bar for aircraft landing pads

6082 and 6061 are both Al-Mg-Si heat treatable strengthen alloys, which have good extrusion
processing and forging properties, and have good anodizing and corrosion resistance. 6082 HBS
> 80after extrusion quenching plus artificial aging,6061is>95.Suitable for the manufacture of
aircraft landing pads, boats, building components, bicycles automotive parts, optical instruments,
rail vehicles, aluminum, etc.6082 and 6061 have many similar uses, but customers in the Middle
East prefer 6082. The 6082 cold drawn extruded aluminum bar has a higher quenching sensitivity
(compared to 6061), and its composition contains Mn, so the corrosion resistance and welding
property are better. The ship board, components etc use more 6082.



Composition of 6082 cold drawn extruded aluminum bar
Si Fe Cu Mn Mg Cr Zn Ti Pb Bi Al
0.7-1.3 ≤0.5 ≤0.1 0.4-1.0 0.6-1.2 ≤0.25 ≤0.2 ≤0.1 Rem

Mechanical properties of 6082 cold drawn extruded aluminum bar

Processing

Temper
mm
Diam
Mpa
Tensile Strength
Mpa
Yield Strength

Elongation
HB
Hardness
精抽
Drawn
T6 ≤40 ≥310 ≥260 ≥10 ≥95
挤压
Extruded
T6 ≤50 ≥310 ≥260 ≥8 ≥95






Aluminium Sheets
Aluminium Sheets

View Details
Aluminium Coils
Aluminium Coils

View Details
Aluminium Foils
Aluminium Foils

View Details
Aluminium Strips
Aluminium Strips

View Details
Aluminium Circles
Aluminium Circles

View Details
Coated Aluminium
Coated Aluminium

View Details
Mirror Aluminum
Mirror Aluminum

View Details
Stucco Embossed Aluminum
Stucco Embossed Aluminum

View Details