6063 Series Extruded Aluminium Flat Bar
We are among the topmost manufacturers, suppliers, and exporters of supreme quality 6063 Aluminum Square Bar. These products are manufactured from high quality aluminum, which is obtained from reliable vendors. The offered bars find vast application in various nuclear reactor components, heat treatment furnace, and petrochemical industries. Our logistic professional ensures that these bars are delivered in stipulated time constraint at customers’ end.
Chemical composition according to EN573-3 (weight%, remainder Al)
| Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Remarks | Each | Total |
|
0.20- 0.60 |
Max. 0.35 |
Max. 0.10 |
Max. 0.10 |
0.45- 0.9 |
Max 0.10 | Max 0.10 | Max 0.10 | Max 0.05 | Max 0.15 |
Alloys and Tempers
Pure aluminum has a conductivity of about 65 percent of the International Annealed Copper Standard (lACS). Aluminum can be produced 99.99 percent pure; however, this purity is costly to achieve and the mechanical properties are low.
Alloy 6063 has been widely used for outdoor high voltage substation buses because of its excellent mechanical and electrical properties and its availability and economy. Where high strength is desirable and conductivity requirements are lower, alloy 6061-T6 bus is used. Where high conductivity is reqnired, with a minimum sacrifice in mechanical properties, alloy 6101 is used in a variety of shapes.
Other aluminum alloys may be used for bus conductors. However, they should be used with care since conductivity and mechanical properties can be greatly affected by small amounts of alloying elements.
Basic info :
Model No : 6063;
Shape : flat;
Grade : 6000 series;
Application : Door & Window, Decorations,Heat Sink,Glass Wall, Transportation Tools;
Temper : T3-T8;
Alloy : Alloy;
Surface Finishing : Mill Finish;
Alloying Ingredient : 6063;
Certification : ISO;
Export Markets : Global;
Mechanical properties according to EN755-2
| Temper* |
Thickness e** |
Yield stress Rp0.2 (mpa) |
Tensile strength Rm (mpa) |
Elongation A[%] |
Elongation A50mm [%] |
Hardness ** HB |
| T4 | e<=25 | 65 | 130 | 14 | 12 | 45 |
| T5 | e<=3 | 130 | 175 | 8 | 6 | 55 |
|
3 |
110 | 160 | 7 | 5 | 50 | |
| T6 | e<=10 | 170 | 215 | 8 | 6 | 65 |
|
10 |
160 | 195 | 8 | 6 | 60 | |
| T66 | e<=10 | 200 | 245 | 8 | 6 | 75 |
|
10 |
180 | 225 | 8 | 6 | 70 |
Additional Info :
Trademark : ;
Packing : Standard Seaworthy Packing;
Production Capacity : 6000 Tons/Month;
Origin : ,China;
Payment Terms : L/C, T/T, Paypal, Money Gram, Western Union;
Trade Terms : FOB, CFR, CIF, FAS, FCA, EXW;
Physical properties (approximate values, 20℃)
|
Density [kg/m3] |
Melting range [℃] |
Electrical Conductivity [MS/m] |
Thermal Conductivity [W/m.K] |
Co-efficient of Thermal expansion 10-6/k |
Modulus of elasticity [GPa] |
| 2700 | 585-650 | 28-34 | 200-220 | 23.4 | ≈70 |
Features :
This is generally considered to be an extrusion alloy that is heat treatable for strengthening
Aluminum bar is an extruded aluminum product available flat, square or rounded
Bar is used for stamping, casting or machining a finished product
Aluminum’s anti-corrosion, high strength, low weight and thermal conductive properties are useful for support, structural and high heat applications
6063 aluminum bar is known primarily as an architectural grade of aluminum due to its attractive, smooth finish
It exhibits the same strength, light weight and anti-corrosion properties as other grades
6063 aluminum is also easy to form, extrude and weld, making it a good material for custom decorative components
Anodizing increases its corrosion-resistance for exposed products
6063 T-52 is an aluminum alloy, with magnesium and silicon as the alloying elements
Generally, it has good mechanical properties and is heat treatable and weldable
6063 is mostly used in extruded shapes for architecture, particularly window frames, door frames, and roofs.
It is typically produced with very smooth surfaces fit for anodizing
It displays very good corrosion resistance, medium fatigue strength and good cold formability
Properties
Aluminium and Copper Specifications
| Parameters | Aluminium | Copper |
| Relevant Standards |
IEC 60105 ISO 209-1,2 |
IEC 60028 |
|
Physical Properties Chemical Composition Specific Heat gm.cal/℃ Density gm/cm2 Melting Point ℃ |
0.092 2.91 660 |
99% pure 0.220 8.89 1083 |
|
Mechanical Properties Ultimate Tensile Strength kgf/mm2 Ultimate Shearing Strength kgf/mm2 Elastic Modulus kgf/mm2 0.2% Tensile-proof Strength kgf/mm2 |
20.5/25 15 6,700 16.5/22 |
22-26 16-19 12000 60-80% of tensile strength |
|
Electrical Properties Specific Resistance ʋʊcm Volume Conductivity ʋʊmm2 Conductivity % IACS Co-efficient of expansion mm/m/℃ |
3.133 31.9 57 2.3*10-5 |
1.7241 58 100 1.73*10-5 |
Production Description :
|
Aluminum Flat Bar Alloy : 6063; Temper: H112, F, T3, T4, T5, T6 Thickness: Up to 200mm Width: Up to 600mm Length: Up to 6000mm Specifications: Ultimate Tensile Strength, psi: 27,000 Yield Strength, psi: 21,000 Hardness: 60 Chromium: 0.1 max Copper: 0.1 max |
Iron: 0.35 max Magnesium: 0.45 - 0.9 Manganese: 0.1 max Remainder Each: 0.05 max Remainder Total: 0.15 max Silicon: 0.2 - 0.6 Titanium: 0.1 max Zinc: 0.1 max Thicknesses: 0.1875" to 4.5" Widths: up to 6" Diameter: 0.1875" to 12.125" Sizes: 0.375" to 6" |
Applications :
Commonly used in the manufacture of furniture, windows, stair rails, and in pipe railing
Commonly used in architectural extrusions
6063 aluminum bar is used for extruded and formed parts that can combine support with decoration
It is used for trim, decorative screens and grates and ornamental frames and supports.