2A04 T4 aluminum alloy rod for rivet
2A04 aluminum alloy rod’s chemical composition:
Silicon Si: 0.30 Iron Fe: 0.30 Copper Cu: 3.2-3.7 Magnesium Mg: 2.1-2.6 Zinc Zn: 0.10 Manganese Mn: 0.50-0.8, Titanium Ti: 0.05-0.40 铍Be: 0.001-0.01 Aluminum Al: Quantity Note: Single: 0.05; Total: 0.10
2A04 T4 aluminum alloy rod’s mechanical properties:
Shear strength τ (MPa): ≥ 275 Note: Natural aging to basic stable shear resistance after wire solution heat treatment. Specimen size: wire diameter ≤ 6.0
Heat treatment specification
1) Rapid annealing: heating 350 ~ 370 C; with the effective thickness of the material, the holding time is 30 ~ 120min; air or water cooled. 2) Quenching and aging: quenching 500 ~ 510 C, air cooling; natural aging room temperature 120h.
Aluminium Sheets
View DetailsAluminium Coils
View DetailsAluminium Foils
View DetailsAluminium Strips
View DetailsAluminium Circles
View DetailsCoated Aluminium
View DetailsMirror Aluminum
View DetailsStucco Embossed Aluminum
View DetailsAluminum
- what are stop sign posts made...
- 3003 Anodised Coil Sheet
- Polyester Film Aluminum Wire
- 5005 h34 aluminum plate
- Comparison of anodized aluminu...
- 2011 T3 T6 T8 aluminum round b...
- 3003, 3105 anodized aluminum p...
- 6082 t651 aluminum plate for a...
- Deep drawing aluminum disc
- aluminum sign manufacturer
- 3102 H22 H18 aluminium foil fo...
- aluminum profile photo frame
- 5052 H38 Aluminum Sign Blanks...
- Aluminum panel sheet
- 7003 T651 T7531 extruded alumi...
- European Aluminum Foil Associa...
- 1100 H22 Aluminum foil for inc...
- Aluminum disc blank
- corrugated aluminum jacketing
- class 200 grade aluminum windi...